MIM mobile card holder mobile card slot
Material: 17-4PH
Tensile strength: ≥ 960 MPa after sintering, ≥ 1150 MPa after heat treatment
Yield strength: ≥ 730 MPa after sintering, ≥ 960 MPa after heat treatment
Hardness: HRC20-25 after sintering, HRC40-45 after heat treatment
Density: ≥ 7.70 g/cm3
Process: MIM, metal powder injection molding, powder metallurgy
Application: Mobile
Metal Powder Injection Molding MIM Material List
| performance | After sintering | heat treatment | C% | NI% | Cr% | Mo% | Cu% | Si% | Fe% | |
|---|---|---|---|---|---|---|---|---|---|---|
| density | >7.80 g/cm3 | |||||||||
| tensile strength | >500 mPa | >1150 MPa | <0.07 | 3-5 | 16-18 | 0.15-0.45 | 3.5-4.5 | <1.0 | ||
| hardness | >120 HV10 | HRC 40-45 | ||||||||
| Elongation rate | >50% | >4.5% | ||||||||
| yield strength | >180 MPa | >960 MPa |