Supply MIM injection molded stainless steel 358 zipper heads
Material: 316L
Tensile strength: ≥ 500 MPa
Yield strength: ≥ 180 MPa
Hardness: ≥ 120 HV10
Density: ≥ 7.80g/cm3
Process: Metal powder injection molding, MIM, powder metallurgy
Application: Smartwatches, branded watches
Metal Powder Injection Molding MIM Material List
| performance | After sintering | C% | NI% | Cr% | Mo% | Si% | Fe% | Mn% |
|---|---|---|---|---|---|---|---|---|
| density | >7.80 g/cm3 | |||||||
| tensile strength | >500 mPa | <0.03 | 12-14 | 16-18 | <2.0 | <1.0 | 2.0-3.0 | |
| hardness | >120 HV10 | |||||||
| Elongation rate | >50% | |||||||
| yield strength | >180 MPa |
Metal Powder Injection Molding MIM Dimensional Accuracy Table
Special tolerance requirements can be achieved through secondary machining, such as CNC, lathe, milling machine, etc
| size | General manufacturing tolerances | General situation | exceptional case |
|---|---|---|---|
| 1-4mm | +/-0.05 | +/-0.05 | +/-0.03 |
| 4-10mm | +/-0.10 | +/-0.07 | +/-0.05 |
| 10-20mm | +/-0.15 | +/-0.10 | +/-0.08 |
| 20-30mm | +/-0.25 | +/-0.15 | +/-0.10 |
| features | General scope | Special scope | |
| Part size | 0.2-50g | 0.09-200g | |
| wall thickness | 0.5mm or above | 0.25 or above |